eSun ePLA-LW Natural 1kg

eSun
Availability:

Out of stock


  • Density as low as 0.54g/cm3
  • Foaming volume ratio 220%
  • Free adjustment of strength and foaming ratio
  • Excellent matte surface effect
  • Good interlayer adhesion
  • Easy to paint
  • Excellent printability

$ 38.86 incl. tax
$ 31.59 excl. tax

Out of stock

Join Waitlist We will inform you when the product arrives in stock. Please leave your valid email address below.

No fields found, please go to settings & save/reset fields

eSun ePLA-LW Natural 1kg

A material specially developed for aeromodelling. The interlayer bonding is stable, and the foaming rate and strength can be controlled by adjusting the printing temperature. Using active foaming technology to achieve lightweight, low-density PLA parts, the foaming volume ratio is 220%, and the density is as low as 0.54g/cm3. Foaming makes the layered pattern almost invisible, and the surface of the printed item is matte and delicate. Under the same model and at the same speed, the  lightweight PLA enables the model aircraft to have a lighter wing load and a lower stall speed, which can greatly improve the performance of the model aircraft.

Description

A material specially developed for aeromodelling. The interlayer bonding is stable, and the foaming rate and strength can be controlled by adjusting the printing temperature. Using active foaming technology to achieve lightweight, low-density PLA parts, the foaming volume ratio is 220%, and the density is as low as 0.54g/cm3. Foaming makes the layered pattern almost invisible, and the surface of the printed item is matte and delicate. Under the same model and at the same speed, the  lightweight PLA enables the model aircraft to have a lighter wing load and a lower stall speed, which can greatly improve the performance of the model aircraft.

Filament Properties Table
3D PRINTING FILAMENTePLA-LW
Density(g/cm3)0.54
Heat Distortion Temp(℃,0.45MPa)53
Melt Flow Index(g/10min)8.1(190℃/2.16kg)
Tensile Strength(MPa)32.2
Elongation at Break(%)68.9
Flexural Strength(MPa)41.31
Flexural Modulus(MPa)1701
IZOD Impact Strength(kJ/㎡)8.58
Durability4/10
Printability9/10
Recommended printing parameters
Extruder Temperature(℃)190 – 270℃
Bed temperature(℃) 45 – 60°C
Fan Speed 100%
Printing Speed 40 – 100mm/s
Heated Bed Optional
Recommended Build SurfacesMasking paper, PVP solid glue, PEI
Weight1 kg