Filament for ELEGOO Rapid PLA+ 3D printer Grey 1.75 mm 1 kg - Specification
Color: GrayFilament type: PLAFilament Diameter: 1,75mmNet weight: 1kgBrands: ElegooRapid PLA+ ELEGOO filament (grey)
Rapid PLA+ (polylactide plus – a biodegradable plant-based material enriched with additives that increase durability) ELEGOO in grey is a filament designed for fast, technical prints. The subdued colour masks minor imperfections and allows you to focus on the shape of the model. The material works well in functional designs, prototypes and structural elements where precision and repeatability are important. The spool contains 1 kg of material.
High-speed performance
The filament melts quickly and flows smoothly from the nozzle, allowing you to print at speeds of up to 600 mm/s (with a suitably adjusted printer). Rapid PLA+ has better flexibility and crack resistance compared to standard PLA, making prints less brittle and more durable. In addition, it conducts heat well, which promotes layer bonding.
Accuracy and convenience
The 1.75 mm diameter and ± 0.02 mm dimensional tolerance ensure even material feed and reduce the risk of nozzle clogging. The material is machine-wound and then manually checked to reduce tangles. The recycled cardboard spool facilitates sorting, and the whole package is vacuum-packed with a moisture absorber, making the material ready for printing immediately after opening.
General
| Manufacturer | ELEGOO |
|---|---|
| Model | 50.203.0116 |
| Colour | Grey |
| Weight | 1 kg |
Recommended print settings
| Drying before printing | 55 ± 5°C |
|---|---|
| Ambient temperature and humidity | ≤ 50°C, ≤ 20% relative humidity (store with moisture absorber) |
| Nozzle temperature | 200 – 230°C |
| Table temperature (depending on printer and surface) | 35–65°C |
| Type of working surface | Textured PEI plate (polyetherimide – durable material that holds prints well) or other compatible plates |
| Print speed | Below 600 mm/s |
Physical properties
| Density | 1.23 g/cm³ |
|---|---|
| Melting point | 160°C |
| Deflection temperature under load | 57°C |
| Softening temperature (Vicat test) | 62°C |
Mechanical properties
| Tensile strength (XY – measured in the horizontal plane of the print, where the material is strongest) | 39 ± 2 MPa |
|---|---|
| Elongation at break (XY) | 8.5% ± 1.2% |
| Flexural strength (XY) | 71 ± 6 MPa |
| Flexural modulus (XY) | 2846 ± 175 MPa |
| Impact strength (XY) | 50.4 ± 2.8 kJ/m² |