Filament for 3D printer ELEGOO PLA Marble 1.75 mm 1 kg - Specification
Color: MarbleFilament type: PLAFilament Diameter: 1,75mmNet weight: 1kgBrands: ElegooELEGOO Marble PLA Filament
The marble-coloured filament from ELEGOO allows you to create unique models with a realistic stone finish. Thanks to additives that give the surface a characteristic marble effect, the prints gain an aesthetic ideal for decorations, figurines or architectural models. The material is based on PLA (polylactide – a biodegradable plant-based plastic), so it is environmentally friendly. The spool contains 1 kg of filament, which is enough for many medium and large prints.
Stable and clean printing
The product has a diameter of 1.75 mm and a very precise dimensional tolerance (± 0.02 mm), which ensures even feeding to the printer without jams. It adheres well to the work table, does not form bubbles or excessive threads (so-called stringing), which minimises material waste and saves time. The result is smooth, durable models with a uniform appearance.
Practical and eco-friendly spools
The filament spools are made of cardboard, which facilitates recycling and reduces the product’s environmental impact. In addition, each spool is precisely machine-wound and manually inspected to prevent tangling. Three holes in the spool allow you to easily check how much material is left.
General
| Manufacturer | ELEGOO |
|---|---|
| Model | 50.203.0113 |
| Colour | Marble |
| Weight | 1 kg |
Recommended print settings
| Pre-print drying settings | 55 ± 5°C |
|---|---|
| Ambient temperature and humidity | ≤ 50°C, ≤ 20% relative humidity (store with moisture absorber) |
| Nozzle temperature | 190 – 230°C |
| Table temperature (depending on printer and surface) | 35–65°C |
| Type of working surface | Textured PEI sheet (polyetherimide – a durable, well-adhering material used as a base for 3D prints) or other compatible surface |
| Print speed | Below 300 mm/s |
Physical properties
| Density | 1.26 g/cm³ |
|---|---|
| Melting point | 158°C |
| Deflection temperature under load | 57°C |
| Softening temperature (Vicat test) | 62°C |
Mechanical properties
| Tensile strength (XY – measurement taken in the horizontal plane of the print, where the material is strongest) | 38 ± 3 MPa |
|---|---|
| Elongation at break (XY) | 10.5% ± 2.1% |
| Flexural strength (XY) | 72 ± 5 MPa |
| Flexural modulus (XY) | 2993 ± 182 MPa |
| Impact strength (XY) | 66.2 ± 3.9 kJ/m² |