DWS Flexa GM08B Black – 0.33KG XFAB Resin for 3D Printer
Availability: within 14 business days
Flexible, rubber-like prototyping. Elastomer with 90% elongation and 95 Shore A hardness.
€174.10 incl. VAT 23%
| Quantity | Discount | Price |
|---|---|---|
| 5-9 | 5% | €165.39 |
| 10-Unlimited | 10% | €156.69 |
DWS Flexa GM08B Black - 0.33KG XFAB Resin for 3D Printer - Specification
Color: BlackBrands: DWSNet weight: 0.33kgResin type: FlexibleResolution: 4KResin for 3D printer DWS Flexa GM08B Black – 0.33KG XFAB
Technical specifications
- Environmental conditions for use: 22°C – 27°C, relative humidity 40% – 60%
- Appearance/colour: Liquid/black
- Density: 1 g/cm³
- Viscosity: 1400 ~ 2100 mPa·s at 25°C
Technical properties of the resin after UV curing
- Elongation at break (%): 30 ~ 60
- Shore hardness (Shore D): 22 ~ 25
- Application: Flexible, rubber-like models
- Environmental conditions for use: 22°C – 27°C, relative humidity 40% – 60%
- Appearance/colour: Liquid/black
- Density: 1 g/cm³
- Viscosity: 1400 ~ 2100 mPa·s at 25°C
Technical properties of the resin after UV curing
- Elongation at break (%): 30 ~ 60
- Shore hardness (Shore D): 22 ~ 25
- Application: Flexible, rubber-like models
Resin for 3D printer DWS Flexa GM08B Black – 0.33KG XFAB
FLEXA GM08B resin is a material developed by DWS for use in stereolithographic 3D printing. It is a resin with flexible, rubber-like properties, designed specifically for DWS printers such as the XFAB 3500SD, 029X and XPRO Q.
Key features
:
- High elasticity and high elongation at break (elongation up to 30-60%).
- Precise and smooth surface of printed models.
- Hardness in the range of 22-25 Shore D after UV curing.
Versatile applications, including prototyping of handles, seals, functional and ergonomic components, and products such as footwear or wearable devices. FLEXA GM08B does not require additional UV curing after printing, which simplifies the production process. This material is available in black, and its transparent version is called FLEXA GM08. The resin has a viscosity of 1400-2100 mPa-s and a density of 1 g/cm³ at room temperature.